《南水北调与水利科技》：南水北调中线穿黄隧道盾构注浆浆材试验（苏华,李珍,汪在芹）（摘要）

摘要：为满足南水北调中线工程穿黄隧洞盾构施工工法要求，对研制开发的水泥-膨润土-水玻璃系双液塑性壁后注浆材料，通过室内模拟注浆试验，重点探讨了材料组分对注浆材料流动性、稳定性、凝胶特性、强度等性能的影响。结果表明：凝胶时间可控制在10S左右；不同配比注浆材料1h单抽抗压强度为0.08-0.12MPa，28d为7.81-8.52MPa；渗透系数为2.0×10-8cm/s；模拟注浆时浆液不被水稀释，充填良好；且不会对地层产生劈裂，也不会向开挖掌子面渗漏。

关键词：盾构；南水北调中线；穿黄隧道

中图分类号：TV68；TV41 文献标识码：B 文章编号：1672-1683（2008）01-0028-05

Grouting Experiment of Shield Tunnel Crossing Yellow River in Middle Route of the South-to-North Water Diversion Project

SU Hua,LI Zhen,WANG Zai-qin

(Department of Structure and Materials,Yangtze River Scientific Research Institute,Wuhan 430010,China)

Abstract:To meet construction requirement of shield tunnel crossing Yellow River in the Middle Line of South-to-North Water Diversion Project,by the simulated grouting experiment indoors we have tested the fluidness,stability,strength and gelling property of the material,which is made from cement,bentonite and water-glass,The results indicate that the coagulate time of material can be controlled in about 10 seconds.The uniaxial strength of one hour changes from 0.08MPa to 0.12MPa,28 day""s strength changes from 7.81MPa to 8.52MPa in different mixed component.The hydraulic conductivity of material is 2.0×10-8cm/s.The material can not be diluted by water and can fill in the interspace fully.

Key words:shield;Middle Route of South-to-North Water Diversion Project;tunnel crossing Yellow River

参考文献：

[1]长江水利委员会长江勘测规划设计研究院.隧道盾构施工技术专题研究报告[R].武汉：长江水利委员会长江勘测规划设计研究院.

[2]王树清，黄良锐，唐丽芳.南水北调中线穿黄隧道工程盾构施工同步材料研究[R].武汉：长江水利委员会长江科学院，1996.

[3]DL/T5150-2001，水工混凝土规程[S].

[4]罗云峰，区希，张厚美，等.地铁隧道盾构法同步注浆用水泥砂浆的试验研究[M].混凝土，2004，（8）：72-75.

[5]郑大锋，邱学青，楼宏铭，等.水溶性高聚物在盾构隧道注浆材料中的应用研究[J].华南理工大学学报（自然科学版），2005（8）：87-90.

作者简介：苏华（1979-）男，广西防城港人，在读硕士，主要从事岩土加固材料方面的研究。

来源：《南水北调与水利科技》2008年第1期